texashuntingforum.com logo
Main Menu
Advertisement
Affiliates
Advertisement
Newest Members
nmmuledeerhunter, Dzia-Dzia, TraeMartin, Beatixre, MooseSteed
71989 Registered Users
Top Posters(All Time)
dogcatcher 110,788
bill oxner 91,416
SnakeWrangler 65,416
stxranchman 60,296
Gravytrain 46,950
RKHarm24 44,585
rifleman 44,461
Stub 43,769
Forum Statistics
Forums46
Topics537,029
Posts9,719,585
Members86,989
Most Online25,604
Feb 12th, 2024
Print Thread
Barrels Hardness #6926093 10/19/17 07:10 PM
Joined: Nov 2005
Posts: 5,306
D
DLALLDER Offline OP
THF Trophy Hunter
OP Offline
THF Trophy Hunter
D
Joined: Nov 2005
Posts: 5,306
Does anyone know what the Hardness reading of most rifles. What do you use to clean the carbon out of a very dirty barrel?





Re: Barrels Hardness [Re: DLALLDER] #6926096 10/19/17 07:14 PM
Joined: Sep 2009
Posts: 18,907
C
ChadTRG42 Offline
THF Celebrity
Offline
THF Celebrity
C
Joined: Sep 2009
Posts: 18,907
Hardness will depend on the type of steel used- stainless, chrome moly, carbon, etc. The barrel mfg would have to tell you this.


[Linked Image]
Custom and Precision Ammunition!!
https://DallasReloads.com/
Type 01 and Type 06 FFL
Re: Barrels Hardness [Re: DLALLDER] #6926117 10/19/17 07:31 PM
Joined: Nov 2005
Posts: 5,306
D
DLALLDER Offline OP
THF Trophy Hunter
OP Offline
THF Trophy Hunter
D
Joined: Nov 2005
Posts: 5,306
Chad, have you checked the Hardness of any barrel? If so what was the reading?





Re: Barrels Hardness [Re: DLALLDER] #6926128 10/19/17 07:40 PM
Joined: Mar 2009
Posts: 4,422
J
jeffbird Offline
Extreme Tracker
Offline
Extreme Tracker
J
Joined: Mar 2009
Posts: 4,422
After experimenting on cleaning suppressor baffles, the best I've found so far is Hoppe's Benchrest.

To clean heavy powder residue build up in a barrel, use Hoppe's Benchrest - not the old No. 9.

Saturate the bore to the point it is dripping out of the barrel.

I literally pour it into the barrel and rotate it 360 degrees to make sure it is evenly distributed.

Prop the rifle in a corner or the safe with the muzzle down in a cup to catch the liquid and leave it for 24 hours.

Put some dry patches or a paper towel in the bottom of the cup first, which helps minimize liquid spills or drips when picking it up.

Push a copper or bronze brush through it several times, more solvent, more patches.

It will come out like goop.

Repeat again for 2 - 3 times, 24 hours or at least overnight of soaking each time, until there is no more crud coming out.

Wipeout is good, but does not provide the same end result at the Hoppe's BR.

Also the Hoppe's Benchrest will not cause pitting like Barnes solvent (which is great for quickly cleaning out copper).








Re: Barrels Hardness [Re: DLALLDER] #6926141 10/19/17 07:52 PM
Joined: Oct 2004
Posts: 39,481
R
redchevy Offline
THF Celebrity
Offline
THF Celebrity
R
Joined: Oct 2004
Posts: 39,481
Used hope's No. 9 growing up as a kid. Now use a foaming bore cleaner comes in a can like shaving cream with a plastic tube on the end you jamb in the chamber and squirt till it comes out the end then let sit.

It has worked well for me and its easy. Spray it, let it sit 15 minutes brush and patch out and repeat if needed.


It's hell eatin em live
Re: Barrels Hardness [Re: DLALLDER] #6926142 10/19/17 07:52 PM
Joined: Sep 2009
Posts: 18,907
C
ChadTRG42 Offline
THF Celebrity
Offline
THF Celebrity
C
Joined: Sep 2009
Posts: 18,907
No, I've never paid attention to it. I know from talking to gun smith's and barrel mfg that the hardness does vary depending on the type of steel used. I know that chrome moly steel is a very hard steel, and will wear out reamers and tools quicker than stainless. My old Sako TRG 42 in 300 WM was a chrome moly steel, and it went 2200 hard rounds of 300 WM, which is pretty good barrel life. I would have to consult the barrel mfg to get precise readings on hardness. Just curious, why the interest in hardness?


[Linked Image]
Custom and Precision Ammunition!!
https://DallasReloads.com/
Type 01 and Type 06 FFL
Re: Barrels Hardness [Re: DLALLDER] #6926178 10/19/17 08:19 PM
Joined: Nov 2005
Posts: 5,306
D
DLALLDER Offline OP
THF Trophy Hunter
OP Offline
THF Trophy Hunter
D
Joined: Nov 2005
Posts: 5,306
Just my curiosity mostly but was wondering if Barrel Hardness has anything to do with the consistent accuracy of some brands.





Re: Barrels Hardness [Re: DLALLDER] #6926180 10/19/17 08:24 PM
Joined: Oct 2004
Posts: 39,481
R
redchevy Offline
THF Celebrity
Offline
THF Celebrity
R
Joined: Oct 2004
Posts: 39,481
Highly doubt barrel hardness is what makes accurate barrels, if that was all there was I'm sure they would all make them hard as hell.

I would bet it has much more to do with fit, finish, consistencey, set up of the equipment etc. wich would support why good barrels cost more, more labor and checking twice before cutting etc. goes into them.


It's hell eatin em live
Re: Barrels Hardness [Re: DLALLDER] #6926188 10/19/17 08:34 PM
Joined: Nov 2014
Posts: 1,177
D
DH3 Offline
Pro Tracker
Offline
Pro Tracker
D
Joined: Nov 2014
Posts: 1,177
Most rifle barrels are somewhere between 53 and 60 on the Rockwell "C" scale. The softer the barrel, the more easily it will foul and be harder to clean. Typical materials are 1024CM (Chrome-Moly) and 400 series stainless steel.


Old age and treachery beats youth and stupid every time!
Re: Barrels Hardness [Re: redchevy] #6926447 10/20/17 01:39 AM
Joined: Dec 2008
Posts: 41,083
J.G. Offline
THF Celebrity
Offline
THF Celebrity
Joined: Dec 2008
Posts: 41,083
Originally Posted By: redchevy
Used hope's No. 9 growing up as a kid. Now use a foaming bore cleaner comes in a can like shaving cream with a plastic tube on the end you jamb in the chamber and squirt till it comes out the end then let sit.

It has worked well for me and its easy. Spray it, let it sit 15 minutes brush and patch out and repeat if needed.


^^What I do.

I really don't want it 100% clean. But after the foam, and as many dry patches as it takes, sometimes 20, when they come out clean, I call it good.


[Linked Image]
800 Yard Steel Range
Precision Rifle Instruction
Memberships and Classes Available
Re: Barrels Hardness [Re: DLALLDER] #6926533 10/20/17 04:02 AM
Joined: Dec 2007
Posts: 1,986
H
HornSlayer Offline
Pro Tracker
Offline
Pro Tracker
H
Joined: Dec 2007
Posts: 1,986
I don't recall anyone ever saying they temper their barrels. What I do know is the button broach peens the rifling surface as it is forced through the bore. So the bore interior hardness will be higher than the outside surface of a broached rifle. When I was growing up there was a man that lived outside of Covington, Tx that made hammer forged barrels when he was a young man. I remember him saying that he cut the rifling into the bore and his barrels didn't last as long as "Button rifles".


They make ammo specifically for hunting for a reason! nidea
Re: Barrels Hardness [Re: DLALLDER] #6926656 10/20/17 12:12 PM
Joined: Sep 2009
Posts: 290
F
furfinrfeather Offline
Bird Dog
Offline
Bird Dog
F
Joined: Sep 2009
Posts: 290
I heard that Ruger used the QPQ process on some barrels. That would make the surface very hard.

Re: Barrels Hardness [Re: DH3] #6926799 10/20/17 01:55 PM
Joined: Sep 2007
Posts: 3,806
T
TDK Online Happy
Extreme Tracker
Online Happy
Extreme Tracker
T
Joined: Sep 2007
Posts: 3,806
Originally Posted By: DH3
Most rifle barrels are somewhere between 53 and 60 on the Rockwell "C" scale. The softer the barrel, the more easily it will foul and be harder to clean. Typical materials are 1024CM (Chrome-Moly) and 400 series stainless steel.


I've turned a lot of barrels, most are in mid 30's on the Rockwell scale, soft. I've NEVER seen a barrel up into the 50's. The go to chrome-moly is 4140. Maybe barrels destined for full-auto are harder...

Last edited by TDK; 10/20/17 02:02 PM.

A.M. Little Bespoke Gunmakers LLC
Re: Barrels Hardness [Re: HornSlayer] #6926802 10/20/17 01:58 PM
Joined: Sep 2007
Posts: 3,806
T
TDK Online Happy
Extreme Tracker
Online Happy
Extreme Tracker
T
Joined: Sep 2007
Posts: 3,806
Originally Posted By: HornSlayer
I don't recall anyone ever saying they temper their barrels. What I do know is the button broach peens the rifling surface as it is forced through the bore. So the bore interior hardness will be higher than the outside surface of a broached rifle. When I was growing up there was a man that lived outside of Covington, Tx that made hammer forged barrels when he was a young man. I remember him saying that he cut the rifling into the bore and his barrels didn't last as long as "Button rifles".


Work hardening is real. That said when cutting barrels down in the bandsaw it doesn't slow down much when the blade gets to the bore. If the bores were 53-60, you would note a discernible difference.

Last edited by TDK; 10/20/17 01:59 PM.

A.M. Little Bespoke Gunmakers LLC
Re: Barrels Hardness [Re: TDK] #6926817 10/20/17 02:06 PM
Joined: Dec 2008
Posts: 41,083
J.G. Offline
THF Celebrity
Offline
THF Celebrity
Joined: Dec 2008
Posts: 41,083
TDK,

Would you be more apt to believe barrels anneal, due to heat and slow cooling?


[Linked Image]
800 Yard Steel Range
Precision Rifle Instruction
Memberships and Classes Available
Re: Barrels Hardness [Re: DLALLDER] #6926827 10/20/17 02:09 PM
Joined: Sep 2007
Posts: 3,806
T
TDK Online Happy
Extreme Tracker
Online Happy
Extreme Tracker
T
Joined: Sep 2007
Posts: 3,806
From normal shooting? No.

Tempering starts at around 350 degrees but has to be held at that temperature for a while, usually two hours. Shooting won't get hot enough.

Could you trash the gun in the process to prove me wrong, sure.

Last edited by TDK; 10/20/17 02:12 PM.

A.M. Little Bespoke Gunmakers LLC
Re: Barrels Hardness [Re: TDK] #6926837 10/20/17 02:18 PM
Joined: Dec 2008
Posts: 41,083
J.G. Offline
THF Celebrity
Offline
THF Celebrity
Joined: Dec 2008
Posts: 41,083
Makes sense.

I know when I'm needing to machine hard steel, that my tooling can't cut, I'll anneal. But I know I way surpass 1000°F.

You're right, it would pretty much take full auto fire, and belt fed to anneal.


[Linked Image]
800 Yard Steel Range
Precision Rifle Instruction
Memberships and Classes Available
Re: Barrels Hardness [Re: DLALLDER] #6926848 10/20/17 02:26 PM
Joined: Sep 2007
Posts: 3,806
T
TDK Online Happy
Extreme Tracker
Online Happy
Extreme Tracker
T
Joined: Sep 2007
Posts: 3,806
Annealing is done at whatever the critical temperature is of said Grade of steel. Usually surpassing 1300f, proper annealing is done to bring the steel down to its softest state. Tempering is done at temperature ranges of around 300-600, and is done to reduce Rockwell hardness by a predetermined amount, not to reach its softest state.

In my experience barrels are mid 30's, which are pretty soft

Action bodies are low to mid 40's unless surface hardened.

Internal parts like triggers and sears are pretty hard, 55-60 for wear resistance.

Last edited by TDK; 10/20/17 02:31 PM.

A.M. Little Bespoke Gunmakers LLC
Re: Barrels Hardness [Re: DLALLDER] #6926854 10/20/17 02:31 PM
Joined: Oct 2004
Posts: 39,481
R
redchevy Offline
THF Celebrity
Offline
THF Celebrity
R
Joined: Oct 2004
Posts: 39,481
TDK, is there a reason barrels are not made harder? Is it because harder metals are more prone to cracking?


It's hell eatin em live
Re: Barrels Hardness [Re: DLALLDER] #6926860 10/20/17 02:36 PM
Joined: Sep 2007
Posts: 3,806
T
TDK Online Happy
Extreme Tracker
Online Happy
Extreme Tracker
T
Joined: Sep 2007
Posts: 3,806
Im not a metallurgist, but that would be my assumption. As you increase hardness you increase wear resistance. Unfortunately you lose elasticity and ductility, important properties for containing repeated pressure.

Last edited by TDK; 10/20/17 02:36 PM.

A.M. Little Bespoke Gunmakers LLC
Re: Barrels Hardness [Re: DLALLDER] #6926861 10/20/17 02:36 PM
Joined: Sep 2006
Posts: 32,442
kmon11 Offline
junior
Offline
junior
Joined: Sep 2006
Posts: 32,442
Knives are in the upper 50s to 60m Roclwell hardness. When working a piece of steel into a knife blade many knife makers will anneal (1000 t0 1200 degrees) the blade material to make it easier to work then temper it in an oven to get it back to the desired hardness, many guard their exact steps for getting their knives to the desired hardness.

I know an old Nickel steel Model 12 barrel didn't seem that hard when I cut it off to 22 inches with a pipe cutter.


lf the saying "Liar, Liar your pants on fire" were true
Mainstream news might be fun to watch
Re: Barrels Hardness [Re: kmon11] #6926865 10/20/17 02:38 PM
Joined: Sep 2007
Posts: 3,806
T
TDK Online Happy
Extreme Tracker
Online Happy
Extreme Tracker
T
Joined: Sep 2007
Posts: 3,806
Originally Posted By: kmon1
Knives are in the upper 50s to 60m Roclwell hardness. When working a piece of steel into a knife blade many knife makers will anneal (1000 t0 1200 degrees) the blade material to make it easier to work then temper it in an oven to get it back to the desired hardness, many guard their exact steps for getting their knives to the desired hardness.

I know an old Nickel steel Model 12 barrel didn't seem that hard when I cut it off to 22 inches with a pipe cutter.


You're using the tempering term incorrectly. Tempering does not increase hardness.


A.M. Little Bespoke Gunmakers LLC
Re: Barrels Hardness [Re: TDK] #6927014 10/20/17 04:40 PM
Joined: Jul 2010
Posts: 746
T
TTUhunter4 Offline
Tracker
Offline
Tracker
T
Joined: Jul 2010
Posts: 746
Originally Posted By: TDK
Originally Posted By: kmon1
Knives are in the upper 50s to 60m Roclwell hardness. When working a piece of steel into a knife blade many knife makers will anneal (1000 t0 1200 degrees) the blade material to make it easier to work then temper it in an oven to get it back to the desired hardness, many guard their exact steps for getting their knives to the desired hardness.

I know an old Nickel steel Model 12 barrel didn't seem that hard when I cut it off to 22 inches with a pipe cutter.


You're using the tempering term incorrectly. Tempering does not increase hardness.


Right. Tempering will reduce both hardness and brittleness.


"God made man, but Samuel Colt made them equal."
Re: Barrels Hardness [Re: DLALLDER] #6927029 10/20/17 04:55 PM
Joined: Jul 2014
Posts: 6,279
onlysmith&wesson Online Content
THF Trophy Hunter
Online Content
THF Trophy Hunter
Joined: Jul 2014
Posts: 6,279
I'd be more interested in knowing if there is positive correlation between hardness and flexural strength. (compressive and tensile not so much) But in reality, I just buy off the shelf rifles with good reputations. It's interesting to think about which physical property would have the most effect on accuracy.

Last edited by onlysmith&wesson; 10/20/17 04:55 PM.

An unethical shot is one you take, that you know you shouldn't.
Previous Thread
Index
Next Thread

© 2004-2024 OUTDOOR SITES NETWORK all rights reserved USA and Worldwide
Powered by UBB.threads™ PHP Forum Software 7.7.3